Pinnacle Polymers™® European Typical Physical Properties
|
|
Product
|
Melt Flow
|
Density
|
Additive Package
|
Tensile Yield Strength
|
Flex Modulus
|
Yield Elongation
|
Notched Izod
|
Gardner Impact
|
Haze
|
FDA
|
UL Listed
|
|
Test Method 1
|
ASTM D1238
|
ASTM D1505
|
|
ASTM D638
|
ASTM D790A
|
ASTM D638
|
ASTM D256
|
ASTM D5420
|
1.27mm Plaque
|
|
|
|
|
grams/10 min
|
g/cc
|
|
kpsi
|
kpsi
|
%
|
ft-lb/in
|
in-lb
|
%
|
|
|
| Homopolymer |
|
|
3
|
0.9
|
N,A
|
5.9
|
310
|
8
|
0.45
|
|
9
|
|
|
|
|
3.5
|
0.9
|
LWCO
|
5.2
|
240
|
10
|
0.7
|
|
|
|
|
|
|
4
|
0.9
|
LWCO
|
5.2
|
240
|
10
|
0.7
|
|
|
|
|
|
|
4.8
|
0.9
|
A
|
5.2
|
240
|
10
|
0.7
|
|
|
|
|
|
|
7.9
|
0.9
|
GP
|
5.1
|
240
|
9
|
0.6
|
|
|
|
|
|
|
11
|
0.9
|
GP
|
5.0
|
240
|
9
|
0.6
|
|
|
|
|
|
|
12
|
0.9
|
GP
|
5.0
|
240
|
9
|
0.6
|
|
|
|
|
|
|
12
|
0.9
|
N,A
|
5.7
|
280
|
8
|
0.7
|
|
|
|
|
|
|
20
|
0.9
|
AG
|
5.0
|
240
|
9
|
0.5
|
|
|
|
|
|
|
21
|
0.9
|
N,A
|
5.7
|
280
|
8
|
0.6
|
|
|
|
|
|
|
22
|
0.9
|
N,A
|
5.8
|
290
|
7
|
0.6
|
|
|
|
|
|
|
25
|
0.9
|
AG
|
5.0
|
235
|
9
|
0.5
|
|
|
|
|
|
|
35
|
0.9
|
N,A
|
5.7
|
273
|
14
|
0.6
|
|
25
|
|
|
|
|
35
|
0.9
|
N,A
|
5.7
|
250
|
8
|
0.6
|
|
|
|
|
|
|
35
|
0.9
|
AG
|
5.0
|
225
|
10
|
0.5
|
|
|
|
|
|
|
55
|
0.9
|
N
|
5.8
|
290
|
8
|
0.5
|
|
|
|
|
|
|
55
|
0.9
|
N
|
5.7
|
290
|
8
|
0.5
|
|
|
|
|
| Impact Copolymer |
|
|
8
|
0.9
|
N,A
|
3.5
|
185
|
11
|
≥6
|
≥320
|
|
|
|
|
|
8
|
0.9
|
LTHA
|
3.4
|
155
|
7
|
≥6
|
300
|
|
|
|
|
|
18
|
0.9
|
N,A
|
4.2
|
215
|
5
|
1.5
|
38
|
|
|
|
|
|
20
|
0.9
|
LTHA,N
|
3.5
|
168
|
7
|
2.6
|
186
|
|
|
|
|
|
20
|
0.9
|
N, A
|
3.5
|
180
|
11
|
≥3.5
|
150
|
|
|
|
|
|
35
|
0.9
|
N,A
|
3.3
|
170
|
6
|
≥3.5
|
200
|
|
|
|
|
|
35
|
0.9
|
N
|
3.3
|
160
|
6
|
≥3.5
|
200
|
|
|
|
|
|
38
|
0.9
|
N
|
4.2
|
213
|
6
|
1.3
|
36
|
|
|
|
|
|
55
|
0.9
|
N,A
|
3.2
|
170
|
5
|
≥2
|
170
|
|
|
|
|
|
65
|
0.9
|
N,A
|
3.5
|
190
|
5
|
≥1.5
|
100
|
|
|
|
|
|
80
|
0.9
|
N,A
|
≥3.0
|
≥155
|
5
|
≥1.8
|
≥135
|
|
|
|
| High Impact Copolymer |
|
|
3.5
|
0.9
|
GP
|
3.2
|
160
|
5
|
≥10
|
≥320
|
|
|
|
|
|
8
|
0.9
|
LTHA
|
3.4
|
150
|
10
|
≥10
|
320
|
|
|
|
|
|
11
|
0.9
|
LTHA
|
3.4
|
150
|
7
|
≥10
|
320
|
|
|
|
|
|
20
|
0.9
|
N,A
|
3.5
|
175
|
6
|
≥10
|
225
|
|
|
|
|
|
35
|
0.9
|
N,A
|
3.1
|
155
|
6
|
≥10
|
300
|
|
|
|
|
|
55
|
0.9
|
N,A
|
3
|
145
|
6
|
≥10
|
275
|
|
|
|
| Random Copolymer |
|
|
20
|
0.9
|
GP
|
3.7
|
137
|
12
|
1.0
|
|
|
|
|
| Enhanced Clarified Random Copolymer |
|
|
12
|
0.9
|
A,C
|
4.1
|
155
|
11
|
1.3
|
|
8
|
|
|
|
|
35
|
0.9
|
A,C
|
3.7
|
137
|
12
|
1.1
|
|
8
|
|
|
|
|
35
|
0.9
|
A,C
|
≥3.5
|
≥130
|
12
|
≥1.0
|
|
9
|
|
|
|
|
55
|
0.9
|
A,C
|
3.8
|
149
|
12
|
0.9
|
|
8
|
|
|
| (1) Test specimens except for melt flow rate were prepared by injection molding. |
| Legend |
C - Clarified
GP - General Purpose
A - Anti-stat
N - Nucleated
LTHA - Long Term Heat stabilized
AG - Anti-Gas Fading
LWCO - Low Water Carry-Over
|
| Material Safety Data Sheet |
|
|
|